Zirconia surface modification by a novel zirconia bonding system and its adhesion mechanism

elsevier-non-solus.png

Publication date: Available online 16 October 2017
Source:Dental Materials
Author(s): Takahiro Murakami, Shinji Takemoto, Norihiro Nishiyama, Masahiro Aida
ObjectiveBonding to zirconia has been of great interest over the last 10–15 years. The aim of this study was to develop a zirconia bonding system and clarify its adhesion mechanism.MethodsA zirconia primer was prepared using tetra-n-propoxy zirconium (TPZr) and water. A silane primer was also prepared using γ-methacryloyloxypropyltrimethoxysilane (γ-MPS) and hydrochloric acid. After the zirconia primer was applied to the oxidized zirconia surface, the silane primer was applied to the ZrO2-functionalized layer and the resin cement was applied to the silane-modified layer. Ceramic Primer II was used as a typical MDP-based ceramic primer. Shear bond strengths were measured using a universal testing machine. To clarify the enhancing mechanism of the zirconia bonding system, X-ray photoelectron spectroscopy (XPS) analyses were performed.ResultsThe zirconia bond strength was affected by the surface wettability of zirconia, and the compositions of TPZr and water utilized in the zirconia primer. When the zirconia primer, consisting of 10μL TPZr and 13μL water, was applied to the zirconia surface that had been oxidized by H2O2 above 10%, the maximum bond strength of 8.2MPa was obtained. The mechanism of the zirconia bonding system was established as follows: the hydrolyzed zirconium species formed a more reactive ZrO2-functionalized layer on the oxidized zirconia surface, and the hydrolyzed γ-MPS species adsorbed on that layer introduces a chemical bonding to the resin.SignificanceThe novel zirconia bonding system enhanced the bonding performance of the resin, and showed a greater bond strength than an MDP-based ceramic primer.



from #ORL-AlexandrosSfakianakis via ola Kala on Inoreader http://ift.tt/2zfoxLy

Δεν υπάρχουν σχόλια:

Δημοσίευση σχολίου